Galvanized Steel Plate

Aisi hot rolled galvanized steel sheet

In order to remove iron oxide on the surface of iron and steel parts, after pickling, it is cleaned in an ammonium chloride or zinc chloride aqueous solution or a mixed solution of ammonium chloride and zinc chloride. And then sent to the hot-dip plating bath. Hot-dip galvanizing has the advantages of uniform coating, strong adhesion and long service life....

Sales hotline+86-531-88752665

Emailsales@zhishangsteel.com

Detailed introduction

Parameter

Technical Standard	EN10147, EN10142, DIN 17162, JIS G3302, ASTM A653
Steel Grade	Dx51D, Dx52D, Dx53D, DX54D, S220GD, S250GD, S280GD, S350GD, S350GD, S550GD; SGCC, SGHC, SGCH, SGH340, SGH400, SGH440, SGH490,SGH540, SGCD1, SGCD2, SGCD3, SGC340, SGC340 , SGC490, SGC570; SQ CR22 (230), SQ CR22 (255), SQ CR40 (275), SQ CR50 (340), SQ CR80(550), CQ, FS, DDS, EDDS, SQ CR33 (230), SQ CR37 (255), SQCR40 (275), SQ CR50 (340), SQ CR80 (550); or Customer’s Requirement
Type	Coil/Sheet/Plate/Strip
Thickness	0.12-6.00mm,or customer's requirement
Width	600mm-1500mm, according to customer's requirement
Type of Coating	Hot Dipped Galvanized Steel(HDGI)
Zinc Coating	30-275g/m2
Surface Treatment	Passivation(C), Oiling(O), Lacquer sealing(L), Phosphating(P), Untreated(U)
Surface Structure	Normal spangle coating(NS), minimized spangle coating(MS), spangle-free(FS)
Quality	Approved by SGS,ISO
ID	508mm/610mm
Coil Weight	3-20 metric ton per coil
Package	Water proof paper is inner packing,galvanized steel or coated steel sheet is outer packing , side guard plate,then wrapped by seven steel belt.or according to customer's requirement
Export market	Europe, Africa, Central Asia, Southeast Asia, Middle East, South America, North America, etc

Description

Hot-dip galvanizing is the reaction of molten metal with an iron substrate to produce an alloy layer, thereby combining the substrate and the plating layer. Hot-dip galvanizing is to pickle iron and steel parts first. In order to remove iron oxide on the surface of iron and steel parts, after pickling, it is cleaned in an ammonium chloride or zinc chloride aqueous solution or a mixed solution of ammonium chloride and zinc chloride.And then sent to the hot-dip plating bath. Hot-dip galvanizing has the advantages of uniform coating, strong adhesion and long service life.

Galvanized sheet advantage

01.Anticorrosive:13 years in heavy industrial areas,50 years in the ocean,104 years in the suburbs and 30 years in cities.

02.Cheap:The cost of hot-dip galvanizing is lower than that of other coatings.

03.Reliable:The zinc coating is metallurgically bonded to the steel and forms part of the steel surface,so the coating is more durable.

04.Strong toughness:The galvanized layer forms a special metallurgical structure that can withstand mechanical

damage during transportation and use.

05.Comprehensive protection:Every part of the plated piece can be galvanized,and is fully protected even in depressions,sharp corners,and hidden places.

06.Save time and energy:Galvanizing process is faster than other coating methods.