Application | making pipes, cutting sheets, making small tools, making corrugated sheets, making container, making fences |
Thickness | 0.12-6MM |
Zinc Coating | Z20-600 |
Technique | Hot Rolled or Cold Rolled Based |
Tolerance | ±1%, 0 |
Processing Service | Welding, Punching, Cutting, Bending, Decoiling |
Skin Pass | Yes |
Oiled or Non-oiled | As customer request |
Width | 60mm-1250mm galvanized steel |
Coil ID | 508/600mm |
Weight | 3-5 tons per coil |
Supplier | HBIS, ShouSteel, AnSteel, Tisco,BaoSteel,Tangsteel,etc |
Surface Treatment | Passivation(C), Oiling(O), Lacquer sealing(L), Phosphating(P), Untreated(U) |
Surface Structure | Normal spangle coating(NS), minimized spangle coating(MS), spangle-free(FS) |
Standard | JIS 3302 / ASTM A653 /EN10143 AISI , ASTM , DIN , GB , JIS G3302 G3312 G3321 , BS |
Guarantee quality | Samples and final Inspection before shipment |
Packing | Bundle, or with all kinds of colors PVC or as your requirements |
Purpose:
Coated steel plate has light weight, beautiful appearance and good corrosion resistance, and can be directly processed, which provides a new type of raw material for the construction industry, shipbuilding industry, vehicle manufacturing industry, furniture industry, electrical industry and so on.
The use of galvanized steel plate for the color coated steel plate, in addition to zinc protection, the organic coating on the zinc layer plays a covering isolation role, can prevent the rust of the steel plate, the service life is longer than the galvanized steel plate, according to reports, the service life of the coated steel plate is 50% longer than the galvanized steel plate.
However, in different regions and different parts of use, the use of the same amount of galvanized, the same coating thickness of the color coated plate, its service life will be very different.
Application of color coated steel plate:
Construction (Outdoor)
Factory, agricultural warehouse, residential prefabricated components, corrugated roofs, walls, stormwater pipes, balcony railings, newspaper stands, cold storage, sales kiosks, rolling shutter doors
Construction (Indoor)
Door, door frame, house light steel structure, screen, ceiling, elevator, stairs, ventilation
Electric appliance
Electrical refrigerator, washing machine, switch cabinet, instrument cabinet, air conditioning, microwave oven, bread machine
Furniture
Radiator, lampshade, wardrobe, table, bed, locker, transportation
Automotive and train interior decoration, partitions, containers, dividers, ship compartments
Other
Whiteboard for writing, dustbin, billboard, clock, typewriter, instrument panel, weigher, camera equipment
Packaging: Galvanized coil is made of rust-proof paper and iron sheet as well as inner corner protector and outer corner protector
hot dip zinc coating(Z) A coating obtained by dipping pre-treated steel strip into molten zinc solution in hot dip galvanizing production line. The zinc content in the molten zinc solution should not be less than 99%.
The surface of the higher surface is allowed to have local defects that do not affect the formability, such as slight scratches, slight indentation, slight pitting, slight roll marks and color difference. Can be processed thickness 1.4-8.5mm, can be cut, open equal service
The characteristics of aluminum alloy plates that do not age when stored at room temperature are called anti-aging stability. Because aging will make the alloy yield point elongation during tensile deformation, resulting in uneven surface deformation and wrinkling during stamping, affecting the appearance of stamping parts
hot dip Zinc-Iron alloy coating(ZF) hot dip galvanizing production line, the pre-treated steel strip is immersed in molten zinc solution to obtain the coating. The zinc content in the molten zinc solution should not be less than 99%. Subsequently, a zinc-iron alloy layer is formed on the entire coating by alloying process, and the iron content of the alloy coating is usually 8~15%.
Electrolytic plate, electrogalvanized zinc layer (Z) is a dense coating obtained by reducing the dissolved zinc ions in the electrolyte through the action of current. The coating consists of more than 99% zinc and does not contain trace elements that are harmful to binder bonding or paint performance.
Cold forming cold rolled low carbon steel plate and steel strip production of cold forming cold rolled low carbon steel plate and steel strip with a thickness of 017mm~3.5mm (hereinafter referred to as steel plate and steel strip). The supplier shall ensure that the surface of the steel plate and steel strip will not rust within 6 months from the date of completion of manufacturing.